Revealing the high sensitivity in the metal toinsulator transition properties of the pulsed laser deposited VO2 thin films

Vanadium dioxide (VO₂) is known as a typical 3d-orbital transition metal oxide exhibiting the metal-to-insulator-transition (MIT) property near room temperature. However, their electronic applications have been challenged by the quality and uniformity of VO₂ thin films. In this work, we demonstrate the high sensitivity in the valence charge of vanadium and the MIT properties of the VO₂ thin films to the deposition temperature. This observation indicates the necessity to eliminate the inhomogeneity in the temperature distribution of substrate during the vacuum-deposition process of VO₂. In addition, a high thermoelectric power factor (PF, e.g., exceeding 1 μWcm⁻¹K⁻²) was achieved in the metallic phase of the VO₂ thin films and this value is comparable to typical organic or oxide thermoelectric materials. We believe this high PF enriches the potential functionality in thermoelectric energy conversions beyond the existing electronic applications of the current vacuum-grown VO₂ thin films.     

Novel energy-saving window coating based on F doped TiO2 nanocrystals with enhanced NIR shielding performance

To reduce the energy consumption of cooling in the hot summer days, searching for novel NIR shielding materials for buildings is of great value. In this report, monodispersed F doped TiO₂ nanocrystals with an average size of 8.6 nm were synthesized as novel solar shielding materials for energy-saving windows. All the products adopted an anatase TiO₂ structure. After doping of F ions, the morphology of TiO₂ was transformed from an irregular shape to a pseudospherical shape. The Raman shift and XPS depth analysis confirmed the successful doping of F⁻ ions into the lattice oxygen sites in the TiO₂ structure. The introduction of F⁻ ions generated free electrons and bulk Ti³⁺ in TiO₂ crystals, which activated a localized surface plasmon resonance (LSPR) absorption in the NIR region. Correspondingly, the NIR shielding performance of the TiO₂ films improved with increasing F doping amounts. The NIR shielding value of the films increased from 1.3% to 43.2% when the molar ratio of F to Ti increased from 0 to 0.3. The reason can be attributed to the enhanced NIR absorption induced by the increased electron concentration after doping of fluorine ions. The F–TiO₂ films showed superior visible transmittance (90.1–96.7%). Moreover, the F–TiO₂ films lowered the indoor temperature of the heat box by 5.3 °C in the thermal tests. Overall, the prepared F–TiO₂ nanocrystals show a great potential to be used for energy-saving windows.     

Relationships of tensile strength with crosslink density for the high-carbon black-filled EPDM compounds with various softeners

Equilibrium swelling and rheological tests were adopted to systematically investigate the effects of softener type and dosage on the crosslink densities. The results turned out that the chemical crosslink density could be distinguished from the physical crosslink density by comparing the results of equilibrium swelling and rheological tests. The liquid butadiene (LB) as a softener leads to the greatest reduction in crosslink density, followed by polyethylene wax (PW) and paraffinic oil (PO). The tensile strength decreases with increasing PO content while shows peak values with increase of LB and PW contents. The dependencies of chemical crosslink density on the aging time under 150°C are quite different for the three softeners, which can be expected from the double crosslinking networks consisting of small softener and large main crosslinking networks. Further investigation has been performed to correlate the tensile strength with chemical crosslink density of ethylene propylene diene monomer elastomer vulcanizates. Three different linear relationships can be obtained for the softeners independent of the aging time. It can now be expected from this study that the role of some new softeners in rubber compounds is not only confined to plasticization but also forms crosslinking networks in the peroxide-cured rubbers.     

Structural and Functional Characterization of the ABCC6 Transporter in Hepatic Cells: Role on PXE,Cancer Therapy and Drug Resistance

Pseudoxanthoma elasticum (PXE) is a complex autosomal recessive disease caused by mutations of ABCC6 transporter and characterized by ectopic mineralization of soft connective tissues. Compared to the other ABC transporters, very few studies are available to explain the structural components and working of a full ABCC6 transporter, which may provide some idea about its physiological role in humans. Some studies suggest that mutations of ABCC6 in the liver lead to a decrease in some circulating factor and indicate that PXE is a metabolic disease. It has been reported that ABCC6 mediates the efflux of ATP, which is hydrolyzed in PPi and AMP; in the extracellular milieu, PPi gives potent anti-mineralization effect, whereas AMP is hydrolyzed to Pi and adenosine which affects some cellular properties by modulating the purinergic pathway. Structural and functional studies have demonstrated that silencing or inhibition of ABCC6 with probenecid changed the expression of several genes and proteins such as NT5E and TNAP, as well as Lamin, and CDK1, which are involved in cell motility and cell cycle. Furthermore, a change in cytoskeleton rearrangement and decreased motility of HepG2 cells makes ABCC6 a potential target for anti-cancer therapy. Collectively, these findings suggested that ABCC6 transporter performs functions that modify both the external and internal compartments of the cells.     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

Inhibited intracrystalline cracks and enhanced electrochemical properties of NCM811 cathode materials coated by EPS

The formation of micro-cracks in Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) cathode particles is an extremely important factor affecting the electrochemical characteristics after long-term cycling. Generally, cracks can be divided into intergranular crack and intracrystalline crack according to their positions. Coating has been confirmed as a highly effective strategy to relieve intergranular cracks. However, the intracrystalline cracks of primary-like particles have rarely been studied. In this work, ethoxy functional polysiloxane (EPS) was directly coated on the surface of original NCM811 by tetraethyl orthosilicate (TEOS) hydrolytic polycondensation method without any additives. Then, the microstructure, micromorphology, surface state and electrochemical properties were investigated in detail by XRD, SEM, TEM, CV and EIS. The results displayed that the micro-cracks of primary-like particles were effectively suppressed under appropriate EPS coating. Accordingly, excellent capacity retention of 95.6% (100 cycles, 1C) and rate performance (144.6 mA h/g, 5C) were obtained. These improved mechanical and electrochemical properties are considered to be related to the EPS stress buffer layer, suppressed oxygen vacancies, inhibited phase transition and reduced volume change.     

Achieving excellent energy storage density of Pb0.97La0.02(ZrxSn0.05Ti0.95-x)O3 ceramics by the B-site modification

The applications of antiferroelectric (AFE) materials in miniaturized and integrated electronic devices are limited by their low energy density. To address the above issue, the antiferroelectricity of the reinforced material was designed to improve its AFE-ferroelectric (FE) phase transition under electric fields. In this present study, the composition of Zr⁴⁺ (0.72 Å) and Ti⁴⁺ (0.605 Å) at B-site of Pb_0.97La_0.02(Zr_xSn_0.05Ti_0.95-x)O₃ ceramics with orthogonal reflections are synthesized via the tape-casting method. These ceramics are modified to enhance their antiferroelectricity by reducing their tolerance factor. A recoverable energy storage density W_rec 12.1 J/cm³ was obtained for x = 0.93 under 376 kV/cm, which is superior value than reported until now in lead-based energy storage systems. Moreover, the discharge energy density can reach 10.23 J/cm³, and 90 % of which can be released within 5.66 μs. This work provides a new window and potential materials for further industrialization of pulse power capacitors.     

一种植物油中苯并（a）芘含量测定的固相萃取前处理方法

为了建立一种准确性高、成本低的植物油中苯并(a)芘测定的样品前处理方法，基于GB 5009.7—2016以自制氧化铝柱为固相萃取柱，采用单因素试验对称样量、洗脱剂量、洗脱流速、吸附剂存放时间、吸附剂量这5个影响植物油中苯并（a）芘洗脱的因素进行研究，优化前处理条件，并对测定方法进行考察。结果表明：优化的前处理条件为称样量0.100 0 g、洗脱剂量120 mL、吸附剂（氧化铝）量22 g、洗脱流速1滴/2 s、吸附剂存放时间少于12周；方法检出限为0.2 μg/L，样品加标回收率为94.23%～100.00%，RSD为1.20%～7.36%；同一样品测定结果与SGS测定值接近，相对平均偏差为2.36%～3.50%。说明本试验方法测定结果准确，可应用于油脂企业植物油中痕量苯并（a）芘的测定。     

Low thermal conductivity in porous SiC–SiO2–Al2O3–TiO2 ceramics induced by multiphase thermal resistance

The introduction of multiple heterogeneous interfaces in a ceramic is an efficient way to increase its thermal resistance. Novel porous SiC–SiO₂–Al₂O₃–TiO₂ (SSAT) ceramics were fabricated to achieve multiple heterogeneous interfaces by sintering equal volumes of SiC, SiO₂, Al₂O₃, and TiO₂ compacted powders with polysiloxane as a bonding phase and carbon as a template at 600 °C in air. The porosity could be controlled between 66% and 74% by adjusting the amounts of polysiloxane and the carbon template. The lowest thermal conductivity (0.059 W/(m·K) at 74% porosity) obtained in this study is an order of magnitude lower than those (0.2–1.3 W/(m·K)) of porous monolithic SiC, SiO₂, Al₂O₃, and TiO₂ ceramics at an equivalent porosity. The typical specific compressive strength value of the porous SSAT ceramics at 74% porosity was 3.2 MPa cm³/g.     

Effect of laser power density on the electrochromic properties of WO3 films obtained by pulsed laser deposition

Pulsed laser deposition (PLD) was used to prepare tungsten trioxide (WO₃) films on ITO substrates with a varying laser power density of 4.0–5.5 W/cm². XPS indicated that when the laser power density decreased, the peak positions of the W 4f and O 1s orbits shifted slightly to low energy due to the difference in oxygen vacancies. As the laser power density decreased, W⁶⁺ gradually replaced the lattice position of O^2?, increasing oxygen vacancies in the lattice. The transmittance modulated values (ΔT) were over 44% at 830 nm, indicating strong absorption by the WO₃ thin films in the near-infrared ray. The switching time of the WO₃ thin films between bleached states and coloured states decreased as the laser power density increased due to the amorphous structure, morphology, and lower oxygen deficiency at a high power density. The high ΔT and very fast switching time of t_b (1.09 s) and t_c (6.01 s) demonstrated the excellent electrochromic (EC) properties of the WO₃ films prepared by PLD.